Classification:
ASTM: B32 Sn40A
Nominal Composition:
Tin 40.00, Lead 60.00
Liquidus:
460 °F
Liquidus:
238 °C
Solidus:
361 °F
Solidus:
183 °C
Classification:
ASTM: B32 Sb5
Nominal Composition:
Tin 95.00, Antimony 5.00
Liquidus:
464 °F
Liquidus:
240 °C
Solidus:
450 °F
Solidus:
233 °C
Classification:
AMS: 4185
Nominal Composition:
Aluminum 88.00, Silicon 12.00
Liquidus:
1080 °F
Liquidus:
582 °C
Solidus:
1070 °F
Solidus:
577 °C
Nominal Composition:
Copper 92.00, Tin 7.70, Phosphorous 0.30
Liquidus:
1880 °F
Liquidus:
1027 °C
Solidus:
1620 °F
Solidus:
882 °C
Classification:
AMS: 4770
Nominal Composition:
Silver 50.00, Copper 15.50, Zinc 16.50, Cadmium 18.00
Liquidus:
1175 °F
Liquidus:
635 °C
Solidus:
1160 °F
Solidus:
627 °C
Classification:
AMS: 4771
Nominal Composition:
Silver 50.00, Copper 15.50, Zinc 15.50, Cadmium 16.00, Nickel 3.00
Liquidus:
1270 °F
Liquidus:
688 °C
Solidus:
1170 °F
Solidus:
632 °C
Classification:
AMS: 4769
Nominal Composition:
Silver 45.00, Copper 15.00, Zinc 16.00, Cadmium 24.00
Liquidus:
1145 °F
Liquidus:
618 °C
Solidus:
1125 °F
Solidus:
607 °C
Nominal Composition:
Nickel 6.00, Copper 55.00, Zinc 35.00, Manganese 4.00
Liquidus:
1685 °F
Liquidus:
920 °C
Solidus:
1615 °F
Solidus:
880 °C
Classification:
AMS: 4775
Nominal Composition:
Nickel 74.00, Chromium 14.00, Silicon 4.00, Boron 3.10, Iron 4.50, Carbon 0.75
Liquidus:
1900 °F
Liquidus:
1038 °C
Solidus:
1790 °F
Solidus:
977 °C
Classification:
AMS: 4777
Nominal Composition:
Nickel 82.40, Chromium 7.00, Silicon 4.50, Boron 3.10, Iron 3.00
Liquidus:
1830 °F
Liquidus:
999 °C
Solidus:
1780 °F
Solidus:
971 °C
Nominal Composition:
Copper 87.00, Manganese 10.00, Cobalt 3.00
Liquidus:
1885 °F
Liquidus:
1030 °C
Solidus:
1760 °F
Solidus:
960 °C
Classification:
AMS: 4778
Nominal Composition:
Nickel 90.90, Silicon 4.50, Boron 3.10, Iron 1.50
Liquidus:
1900 °F
Liquidus:
1038 °C
Solidus:
1800 °F
Solidus:
982 °C